[摘要] 通過6根玄武巖纖維布加固損傷鋼筋混凝土梁和2根未加固梁進(jìn)行靜力抗彎性能試驗研究，研究了玄武巖纖維布加固既有損傷混凝土梁的破壞特征、抗彎承載力、撓度等，并分析了不同粘貼層數(shù)對加固效果的影響。試驗表明:加固梁抗彎承載力隨纖維布粘貼層數(shù)增加而提高，粘貼5層時提高約為80%，粘貼層數(shù)與提高幅度不成線性關(guān)系；隨纖維布粘貼層數(shù)增加，加固梁發(fā)生纖維布剝離破壞風(fēng)險增大。
[關(guān)鍵詞] 玄武巖纖維布；加固損傷混凝土梁；抗彎性能
中圖分類號：TU375.1 文獻(xiàn)標(biāo)識碼：A 文章編號：1002-848X( )
作者簡介：王海良，教授，碩導(dǎo)，Email:wanghailiang6601@126.com。
Experiment study on flexural behavior of damaged RC beams strengthened with basalt fiber
reinforced polymer
Wang Hailiang, Zhang Jing, Yang Xinlei, Ren Quanchang, Dong Peng
(
Abstract: Based on the monotonic loading tests on six beams strengthened with basalt fiber reinforced polymer and two control specimens, the failure mode, flexural bearing capacity, deflection, etc., were investigated, and the influence of layers of BFRP sheets was analyzed. Results showed that the bearing capacity of the damaged reinforced beams strengthened with basalt fiber was enhanced with the BFRP layers increasing, and the relationship was not linear; when five layers were pasted, the bearing capacity of the specimen increased by 80%；With the increase of paste layers of the fiber cloth, the peel failure mode occurred more frequently.
Keywords: basalt fiber reinforced polymer; strengthened damaged RC beams; flexural behavior
參 考 文 獻(xiàn)
[1] 楊勇新,楊 萌,趙 顏等.玄武巖纖維布的耐久性試驗研究[J].工業(yè)建筑,2007,37(6):11-13.
[2] 謝爾蓋,李中郢.玄武巖纖維材料的應(yīng)用前景[J].纖維布料,2003,20( 3):17-20.
[3] 楊勇新，岳清瑞.玄武巖纖維及其應(yīng)用中的幾個問題[J].工業(yè)建筑,2007,37(6):1-4.
[4] 陳緒軍,楊勇新,邢建英,等.玄武巖纖維布加固鋼筋混凝土梁抗彎試驗研究[J].鄭州大學(xué)學(xué)報：工學(xué)版.2009(2):61-65.
[5] 孫衍英,劉伊琳,胡海濤.玄武巖纖維布加固鋼筋混凝土梁受力性能的研究[J].青島理工大學(xué)學(xué)報. 2010(1):29-32.
[6] 歐陽煜,王鵬,李翔.玄武巖纖維布加固鋼筋混凝土梁受彎試驗研究[J].建筑結(jié)構(gòu).2008(11):74-77.
[7] 丁斌，余江滔，歐陽利軍，等.玄武巖纖維布加固混凝土連續(xù)梁實驗研究[C]//第八屆全國地震工程學(xué)術(shù)會議論文集（Ⅱ）.2010:613-615.
[8] 李志強,麻建鎖,白潤山,等.玄武巖纖維布提高鋼筋混凝土梁受剪承載力試驗研究[J].河北建筑工程學(xué)院學(xué)報，2008(3):7-8.
[9] 周長東.玻璃纖維聚合物加固混凝土橋梁力學(xué)性能研究 [J].橋梁建設(shè).2004(5):73-76.